Our Organic Zircon uses 100% TOSOH powder because dental technicians say it's the best!

The unique production of our blanks is based on the patented Single CIPTM technology. At the beginning of this
process, the powder mixture is axially prepressed in a mold much more slowly than usual, so that the individual grains can be
grains can distribute themselves more evenly in the blank. Subsequently, each blank produced in this way is individually vacuum-packed
and pressed together isostatically at constant pressure from all directions in a controlled manner at all times.
This results in a further 3% shrinkage. Only this procedure guarantees absolutely homogeneous blanks
with uniform particle size distribution and flexural strength, uniformly defined shrinkage and an extremely high degree of translucency.
extremely high degree of translucency. In the next step, these blanks are sintered to only 23%.
- a value that is deliberately 2-3% lower than that of other manufacturers. The material becomes more chalky and qualitatively
less brittle in milling behavior. This reduces edge chipping and increases the service life of the milling tools. Finally, each blank is brought to final size and ultrasonically inspected for perfection.
All blanks produced to the highest industrial standard exhibit improved hydrothermal aging behavior in accordance with DIN EN ISO 13356. The maximum value of the monoclinic phase after artificial aging of 7 % by volume is far below the limit of 25 % by volume specified in the standard, and the flexural strength significantly exceeds the value required by the standard. To simplify the laboratory workflow, all Organic
Zirconia restorations can be processed at a sintering temperature of 1,450 °C / 2 hours holding time.